Hanhai 3 LAYERS ABS TWO PIPE STADARD OPERATING PROCESS

Installation Note: According to the red mark, the host and the inverter correspond one by one, connect the main motor wire, and connect the heating wire and the fan wire to the terminal block in the main electric box according to the signal mark.

Hanhai three layers ABS two pipe machine Temperature settings:

65 host A (outer layer) barrel 1 area 165 degrees, barrel 2 area 168 degrees, barrel 3 area 170 degrees, barrel 4 areas 172 degrees.

65 host B (core layer foaming) the first area of the barrel is 165 degrees, the second area of the barrel is 168 degrees, the third area of the barrel is 170 degrees, and the fourth area of the barrel is 172 degrees.

55Z main engine (inner layer) barrel 165 degrees, barrel 2 170 degrees, barrel 3 172 degrees.

Mold temperature: mold zone 1 – mold zone 17: temperature set to 170 degrees.

Note: ABS material is different, the temperature is different, fine-tune the temperature according to the actual test situation

The foaming density of the core layer can be controlled according to the temperature of the barrel,and the temperature can be fine-tuned  

Start-up speed: First, start the three main engines to set the speed to 200 rpm, start the green button, extrude the plastic from the mold, adjust the eccentric extrusion and connect it to the traction pipe, and pass through the vacuum water tank, spray box, and traction machine for production. After cutting through the cutting machine, measure the thickness of the pipe diameter, adjust the speed of the tractor to reach the standard size, and finally open the main engine linkage and main traction linkage, set the step length to 10, increase the speed of the 65A main engine (press the + key), three main engines and two Traction automatically accelerates at the same time to achieve linkage.

Host linkage: Through the speed regulation of host A, the three hosts are automatically synchronously adjusted.

Note: The speed of the three mainframes can be adjusted by their respective speeds without the use of linkage, and the speed of each layer can be adjusted according to the actual situation of the product.